The use of eco-friendly corrosion inhibitors in metallurgical processing has increased interest due to the reduced environmental impact. Hence, the inhibitory effect of Aniba canelilla (Lauraceae) extract was studied in the corrosion of carbon steel in 1.0 mol∙L-1 hydrochloric acid solution. This acid is used during the surface treatment of steel processing. The carbon steel protection was observed by varying the extract concentration from 50 to 300 mg∙L-1. Polarization curves revealed that this extract acted as an adsorption inhibitor decreasing both anodic and cathodic current densities. A relatively high inhibition corrosion efficiency, close to 97%, was obtained with plant stem extracts by gravimetric measurements. Weight loss measurements showed that the extract remains active for at least 72 hours at room temperature. The adsorption process of this extract is properly represented by the Langmuir isotherm. Atomic force microscopy shows that inhibited acid medium produces a smooth surface.

The inhibitory effect of Bauhinia purpurea (Fabaceae) extract was studied in the corrosion of carbon steel in 1.0 mol∙L-1 sulfuric acid solution. This plant was collected from the Brazilian rainforest. The carbon steel protection was observed by varying the extract concentration from 50 to 500 mg∙L-1. Polarization curves revealed that this extract acted as an adsorption inhibitor decreasing both anodic and cathodic density currents. Weight loss measurements showed that the extract remains stable for at least 72 hours. The adsorption process of this extract obeyed the Langmuir adsorption isotherm. Lastly, Arrhenius plot suggested the physical adsorption of the extract.

Fresh water sponge was used as a silica source for the synthesis of MCM-41 via the hydrothermal process. The silica was extracted from the sponge by washing with nitric acid and piranha solution. Synthesis of MCM-41 was performed at 100 °C for 5 days and the procedure was optimized, with modifications made to the leaching temperature of the silica and the synthesis of mesoporous material, which was characterized by XRD, FT-IR, SEM and adsorption of N2. The optimal result was achieved at a temperature of 135 °C for 3 days, showing ordered mesoporous material with a surface area of 1080 m² g-1.

The aim of this work was to study the phytochemical and antifungal activity of anthraquinones and root and leaf extracts of Coccoloba mollis on phytopathogens. The chemical analysis of ethanolic extracts showed a mixture of long-chain hydrocarbons, carboxyl esters and 3-taraxerone in the leaf extract. Two anthraquinones (emodin and physcion) were isolated and identified from the root extract. Phytochemical screening using the pharmacognostic methods revealed the presence of flavonoids and tannins in the leaves and roots. Anthraquinones were only found in the root extract, no alkaloids, coumarins, saponins and simple phenolics were present. The antifungal activity of C. mollis extracts and anthraquinones isolated from the root of this plant against Botryospheria ribis, B. rhodina, Lasiodiplodia theobromae and Fusarium sp showed promising results for their use as fungicides, where emodin was the most active compound, which inhibited the microorganisms tested up to 44%.